Pacific Northwest Laboratory is developing in situ vitrification (ISV) as a potential remedial action technique for previously disposed radioactive liquid drain sites. The process melts the contaminated soil to produce a durable glass and crystalline waste form and encapsulates the radionuclides. The development of this alternative technology is being performed for the U.S. Department of Energy. The results of an ISV pilot-scale test conducted in June 1983 are discussed in which soils contaminated with actual radioactive trans-uranic and mixed fission product elements were vitrified. The test successfully demonstrated the containment of radionuclides during processing, both within the vitrified mass and in the off-gas system. No environmental release of radioactive material was detectable during testing operations. The vitrified soil retained >99% of all radionuclides. Losses to the off-gas system varied from ≤0.03% for particulate materials (plutonium and strontium) to 0.8% for cesium, which is a more volatile element. The off-gas system effectively contained both volatile and entrained radioactive materials. Analysis of the vitrified soil revealed that all radionuclides were distributed throughout the vitrified zone, some more uniformly than others. Analysis of soil samples taken adjacent to the block indicated that no migration of radionuclides outside the vitrification zone occurred. Leaching studies have shown that the ISV process generates a highly durable waste form, comparable to Pyrex and granite. Based on geologic data from the hydration of obsidian, which is chemically similar to the ISV glass, the hydration or weathering rate is predicted to be much less than 1 mm in 10000 yr.